•  Equipment: ball-interfaced and anvil interface micrometer, deflectometer, conditioning chamber, environmental test chamber are recommended but not required.

• Apparatus: The machine will have a stationary and movable head, the machine should be able to indicate the total force being carried by the test specimen, it will either be a 3- or 4-point bend test. Below is what they used

• Test at least five specimens.

• Condition the specimen in a chamber if the test environment is not the same as a conditioned environment.

•   Measure the length, width and thickness at three places in the specimen.

• Place the specimeninto the test fixture and align the fixture so the longitudinal axis of the specimen is perpendicular (within 1 degree) to the longitudinal axes of the loading bars, the bars must also be parallel (within 1 degree) to the plane of the specimen facings.

•   Attach the deflection transducer.

• Apply a compressive force to the specimen until failure or until a deflection equal to the thickness is reached.

• It was noted that the speed of testing should be around 6mm/min. 

• Failure should occur at 3-6 minutes.

• 3-point or 4-point bend test

• Force versus crosshead displacement, force versus deflection data continuously, or at frequent intervals (around 2-3 recordings per second, with a target minimum of 100 recorded data points)

• If there are any initial failures, record force, displacement and mode of damage where the failure occurs. 

• Record mode, area and location of each failure. 

• Use the failure identification codes

• Record the max force, failure force, head displacement and the deflection at the moment of ultimate failure. 

• For ultimate failure modes, record the mode, area and location of ultimate failure for each material. 

• Calculations:

  • For 3-Point Mid-Span Loading:

    • Core Shear Ultimate Stress

    • Core Shear Yield Stress

    • Facing Stress

  • For 4-Point, Quarter-point loading:

    • Core Shear Ultimate Stress

    • Core Shear Yield Stress:

    • Facing Bending Stress

  • For 4-Point (Third Point) Loading:

    • Core Shear Ultimate Stress

    • Core Shear Yield Stress:

    • Facing Bending Stress:

these calculations are in the confluence page

• Test at least 5 specimens

• Measure the specimen in 3 places and report average thickness and width as well as average area. 

• The speed of testing should be able to have a nearly constant strain rate and it will produce failure within 1 to 10 min. 

• Tensile Test

• Calculate modulus of elasticity

• Calculate ultimate tensile strength. 

• If tensile modulus/ultimate tensile strain will be calculated, get the tensile strain at the indicated displacement at each required data point. 

• Tensile chord modulus of elasticity.

• Poisson’s Ratio by Chord Method.

*All these equations are found in the confluence page*

• Equipment required:

  • Micrometers/calipers

  • Strain-Indicating Device

  • Bonded Resistance Strain Gauges

  • Emery cloth

  • Special Alignment Jig (pictured below)

• Compression Testing Fixture(pictured below are schematics and the actual fixture)

• Apparatus:

  • There will be a force indicator

  • The machine will have two loading heads. 

^^^I don’t exactly know what this means (interpret pls)

• The drive mechanism will be able to give a controlled displacement rate with respect to the stationary head. 

• If the atmosphere conditions suck use a conditioning chamber and an environmental test chamber.

• If the material is super stiff use an extensometer. 

• Test at least five specimens per test condition

• Get ready because this is a HEFTYYY procedure 

• General instructions:

  • Condition specimens before/after strain gaging as required. Condition travelers if they will be used

  • Apply strain gages/extensometers to both faces of the specimen

  • The loading rate should produce a failure within 1 to 10 min. 

    • Strain-Controlled Tests, standard strain rate of 0.01 min/1 ?? I think the unit may be wrong here. I think it's supposed to be mm/min??

    • Constant Head-Speed Tests, A standard crosshead displacement of 1.5mm.min. 

  • Monitor test temp by placing a thermocouple within 25mm of the specimen gauge section. You can also tape the thermocouple(s) to the test specimen and travelers. 

• Fixture Installation:

  • Place the lower wedge housing block on the lower platen, then attack the upper wedge housing block to the upper crosshead/insert it into the upper wedge housing holding fixture, centered over the lower wedge housing block. 

  • Move a crosshead to close the distance between the 2 housing blocks while guiding the bearing guide rods into the mating bearing of the companion housing block. The lower housing block can be fitted with guide rods long enough to allow the rods to remain in the bearings while the wedges or specimen assembly is loading into and out of the housing blocks. 

• Specimen Insertion:

  • If needed, move the testing machine crosshead to open the distance between the 2 housing blocks so both the upper and lower wedge rip assemblies may be accessed. 

  • I’m so sorry but idk how to summarize the following thing :(

• If the specimen will be aligned with the wedge grips in the fixture housing block, the lower jaws should be raised so that grip-faces open to allow specimen insertion.

• If we need to, free the upper wedge grips so they are in the fully open position. Moving the crosshead, close the distance between the housing blocks and guide the upper end of the specimen into the opening between the upper wedge grips. 

• Close the upper grips manually to check the specimens vertical displacement. Do it with the lower grips as well. The upper grips should be in full contact with the wedge when closed. Repeat if we need to. 

• Keep the grips closed and slowly close the distance between the housing blocks by moving the crosshead, watch the force indicator at this time. Stop the crosshead when the specimen begins to take a compressive force. 

• Transducer Installation:

  • If the strain-transducer(s) other than strain gages will be used, attach them to the specimen at the mid-span, mid-width location. Then, attach the strain recording instrumentation to the strain gages or other transducers on the specimen. Then, remove any remaining preload and zero the transducer(s).

• Loading:

  • Apply the force to the fixture at the specified rate until failure while recording data.

• https://www.youtube.com/watch?v=qfHoq9w3glE I really like this video

• Same as the above standard.

• Test at least five specimens per test condition

• Same as the above standard as well as:

  • This test will have normal strain instrumentation in both the longitudinal and transverse directions. It will also have a continuous/nearly continuous force normal strain data recording. 

• Same as the above standard.

• Calculations:

  • Max shear stress/shear stress

  • Shear strain/max shear strain

  • Shear modulus of Elasticity

  • Offset Shear Strength

  • Various statistics

*Again, all these formulas will be in the confluence page*

• Apart from the testing apparatus, the only equipment needed is a conditioning room/desiccators

• The following is a picture of the testing apparatus:

• Test at least 10 specimens for each adhesive we want to test

• Remember, I couldn’t understand this one :C sorry

Image Removed

Image Removed

• Hehe…remember this…yeah it still makes no sense :C

Image Added

Image Added

• Ummm...help

• These are the only values needed to be reported (they don’t seem like they’re calculations)

  • Average peel/stripping strength.

  • Max and Min strength values of the series.

  • Type of failure.

• Will conform to the following geometry:

  

• No equipment listed, just apparatus:

  • The machine will have a capacity of no less than 6810kg in compression and shall be fitted with a shearing tool containing a self-aligning seat to ensure uniform lateral distribution of the load.

  • It will be able to maintain a uniform rate of loading so the load may be applied with a continuous motion. The apparatus is pictured below:

• I don’t really get how to explain this one to be honest help :C

• Calculations:

  • Shear stress at failure.

  • Max and min shear stress at failure and percentages of wood failure.

  • The standard deviation of all individual test values.

  • Average shear stress at failure and the average percentage of wood failure.

• Use these if you can:

• Prepare at least 10 specimens in the case of metal-to-metal specimens.

• Place the Put the specimen in the jig in the vise of the impact machine so the specimen butts squarely against the training end of the jig. 

• Rest the impact head of the machine against the specimen , then and adjust the jig so the head fits squarely against the impact face of the specimen.

• Raise the impact head to a certain height and release the safety catch. Then we will have to read the energy absorbed by the impact

• We will then note the impact energy absorbed.

• A pendulum will fall and hit our specimen and test the adhesive strength

• Substrates—Fiber reinforced plastic (FRP) as specified, with metal composition (heat treat, temper, and condition) and roughness as specified when bonding FRP to metal. (I don’t know what this means)

• Cut fiber-reinforced plastic parts into flat coupons 1 by 4 in. (25.4 by 100 mm) at a nominal thickness of 0.1 in. (2.5 mm). In the case of FRP-to-metal bonding, use metal with a nominal thickness of 0.06 in. (1.5 mm). It is recommended that a diamond tip water-cooled saw blade be used, or a cutting method capable of producing sharp cut edges.

• Joint Geometry—Control joint geometry by appropriate fixturing, using glass beads or other suitable means to control a 0.03-in. (0.76-mm) adhesive bondline thickness. Use the minimum number of glass beads in the glue line needed to hold bondline thickness. Fixturing pressure is allowed. Lap shear overlap will be 1 by 1 in. (25.4 by 25.4 mm) See Figure 1 below.

• No equipment is outlined, only an apparatus which is said to most likely just be a simple tensile tester like pictured below

• Prepare a minimum of 5 lap shear samples in each case and test.

• Prep the surface of the FRP as recommended by the adhesive manufacturer. If there is no recommendation, prep the surface as outlined in practice D2093. 

• Apply the adhesive in accordance with the adhesive suppliers recommendations. 

• Adhesive Cure—Cure the adhesive at room temperature or elevated temperature using prescribed conditions determined by the adhesive supplier.

• The initial grip separation is 75mm, with a minimum of 25.4mm of each sample end held in the test grips.

• The load rate is 13mm/min. 

• This load rate is said to be an important difference compared to other standards. 

• Tensile test.